Alkyl phenolic resin for adhesive

Alkyl Phenolic Resin (SP: 118-125℃)

Item no.: APU-20-58G

  • Key features:
    - Softening point (Ring & Ball): 118-125℃
    - Enhance the adhesion strength
    - Increase the phasing stability
    - Increase the heat resistance
    - Improve the tackiness retention time
Add to inquiry cart

Product Introduction

Application
Printing coating agents, adhesive tackifier, printing ink, paint, synthetic leather and PVC leather to enhance the adhesive viscosity.
Introduction
Though chloroprene rubber has an excellent weathering, oil and chemical resistance, it is necessary, in practice, to make use of a modifying agent to improve the properties of chloroprene rubber adhesive, such as tackiness retention time, phasing stability, heat resistance and adhesion strength. Alkyl phenolic resin for adhesive“APU-20-58G” is excellently compatible with chloroprene rubber and an indispensable modifying agent for chloroprene rubber for manufacturing adhesive to meet specific purposes.
Alkyl phenolic resin
1) Specifications
ITEM NO. Appearance MgO Reactivity (%) Softening point (℃, R&B)
APU-20-58G Pale yellow, lump 6.8 118-125
2) Typical Formulation (MgO Pre-reation)
Part 1 Parts by wt.
Chloroprene TA-50 100
MgO 4
ZnO 5
Stabilizer 2
Part 2 Parts by wt.
APU-20-58G 50
Toluene 150
MgO 5
Water 0.5
Part 3 Parts by wt.
Toluene 96
n-Hexane 123
Ethyl acetate 123
(Solvent formula in total : Toluene/n-Hexane/Ethyl acetate = 2/1/1)

Procedure
Mix ingredients of Part 1 together on milling roll then dissolve in mixed solvent (Part 3). Stir Part 2 in a vessel for 5 hours, then add it the mixture of Part 1 and Part 3. Keep agitation further 5 hours to give adhesive of 25% solids.
3) Adhesive Properties
  Adhesion Strength Tackiness
Retention
Heat
Resistance
Phasing
Resistance
After 5 hours After 24 hours 於60℃
APU-20-58G A-B A A-B C A-B B
A: Excellent
B: Good
C: Fair
D: Poor
a) Heat Resistance
ITEM NO. Heat Resistance (℃) Result
APU-20-58G 90 A-B
Test Conditions
Method ASTM-D-816-55
Weight 500g
Adherend Steel to vulcanized rubber
Test Conditions Kept 3 days after bonding
Temperature graduation 2℃/5 min
b) Phasing Resistance
Adhesives in stoppered jar were kept for one month at 20℃ then phasing was observed
Excellent Completely no phasing
Good Top part is slightly phasing
Fair 5% of upper part is phasing
Poor 50% of adhesive is phasing
c) Tackiness Retention Time
ITEM NO. Tackiness Retention Time Result
APU-20-58G 9 min, 30 sec. D
d) Adhesion Strength

Test Conditions
Peeling angle 180°
Adhesion strength at 60℃ Test pieces were kept 3 days after bonding then kept one hour at 60℃ before test.
Adherend Steel to canvas
Peeling velocity 200 mm/min
Temperature 20℃ (68℉)
ITEM NO. Elapsed Days At 60℃ Initial Strength
1 3 7 Result 1 hour Result 5 hour Result
APU-20-58G 5.6 12.0 15.0 A 7.2 A-B 3.1 A-B
Unit : kg/25 mm
e) Shear strength
Shearing velocity 50 mm/min
Glued area 10 mm x 25 mm
Test Conditions at 20℃ (68℉)
Open time 10 min
Bonded material Plywood to plywood
ITEM NO. Elapsed Days Result
1 3 7
APU-20-58G 24.2 33.2 44.2 B
Unit : kg/25 mm2
Taiwan PU Corporation is a professional alkyl phenolic resin manufacturer, alkyl phenolic resin producer. We supply high quality alkyl phenolic resin products, have an experienced technical team and offer the best price to alkyl phenolic resin.

Alkyl phenolic resin is called phenolic resin for glue, phenolic resin tackifier for glue, phenol formaldehyde resin for glue. If alkyl phenolic resin is needed, please contact us.